Effects of thermal treatment on the adhesion strength and osteoinductive activity of single-layer graphene sheets on titanium substrates

Evidence from laboratory and animal studies provides groundwork for understanding mechanisms and potential before human studies continue.

• Level A · Stronger Clinical Evidence
• Level B · Emerging clinical evidence with positive signals
• Level C · Early human research exploring benefits
• Level D · Scientific groundwork from lab and animal studies
• Emerging · Emerging topic under active research

Abstract (original English)

In recent years, dental implants have become the preferred approach for the restoration of missing teeth. At present, most dental implants are made of pure titanium, and are affected by peri-implantitis and bone resorption, which usually start from the implant neck, due to the complex environment in this region. To address these issues, in this study we modified the surface of titanium (Ti) implants to exploit the antibacterial and osteoinductive effects of single-layer graphene sheets. Chemical vapor deposition (CVD)-grown single-layer graphene sheets were transferred to titanium discs, and a method for improving the adhesion strength of graphene on Ti was developed due to compromised adhesion strength between graphene and titanium surface. A thermal treatment of 2 h at 160 °C was found to enhance the adhesion strength of graphene on Ti to facilitate clinical transformation. Graphene coatings of Ti enhanced cell adhesion and osteogenic differentiation, and imparted antibacterial activity to Ti substrate; these favorable effects were not affected by the thermal treatment. In summary, the present study elucidated the effects of a thermal treatment on the adhesion strength and osteoinductive activity of single-layer graphene sheets on titanium substrates.

Evidence level

Evidence from laboratory and animal studies provides groundwork for understanding mechanisms and potential before human studies continue.

Browse all related research

Filter the research library by this study's title keywords, author, or publication year.