Generation of functionalized polymer nanolayer on implant surface via initiated chemical vapor deposition (iCVD).

Evidence from laboratory and animal studies provides groundwork for understanding mechanisms and potential before human studies continue.

• Level A · Stronger Clinical Evidence
• Level B · Emerging clinical evidence with positive signals
• Level C · Early human research exploring benefits
• Level D · Scientific groundwork from lab and animal studies
• Emerging · Emerging topic under active research

Abstract (original English)

Initiated chemical vapor deposition (iCVD) was utilized to generate a 200nm thick, uniform, functionalized polymer nanolayer comprised of glycidyl methacrylate (GMA) on the surface of titanium implants as a means to improve cellular attachment. Dot-patterned GMA-coated specimens were prepared as well as fully coated specimens. In vitro cellular responses, including cell morphology, protein adsorption, cell proliferation assays, alkaline phosphate activity (ALP) assays, and calcium deposition assays were studied using adipose derived stem cells. The mechanical stability of the thin film was investigated by XPS and FE-SEM analysis of the GMA-coated implant after implantation to an extracted bone from a pig. The GMA-coated specimens displayed increased protein adsorption, higher alkaline phosphatase activities, and higher calcium deposition as compared to control sample with no cytotoxicity. Additionally, no defect was observed in the test of mechanical stability. Notably, dot-patterned GMA-coated samples displayed higher alkaline phosphatase activities than others. Functionalized polymer nanolayer deposition via iCVD is a flexible and robust technique capable of mass production of biocompatible layers. These properties make this technique very suitable for implant applications in a variety of ways.

Evidence level

Evidence from laboratory and animal studies provides groundwork for understanding mechanisms and potential before human studies continue.

Browse all related research

Filter the research library by this study's title keywords, author, or publication year.