Material extrusion additive manufacturing of poly(lactic acid)/Ti6Al4V@calcium phosphate core-shell nanocomposite scaffolds for bone tissue applications.

Evidence from laboratory and animal studies provides groundwork for understanding mechanisms and potential before human studies continue.

• Level A · Stronger Clinical Evidence
• Level B · Emerging clinical evidence with positive signals
• Level C · Early human research exploring benefits
• Level D · Scientific groundwork from lab and animal studies
• Emerging · Emerging topic under active research

Abstract (original English)

The use of porous scaffolds with appropriate mechanical and biological features for the host tissue is one of the challenges in repairing critical-size bone defects. With today's three-dimensional (3D) printing technology, scaffolds can be customized and personalized, thereby eliminating the problems associated with conventional methods. In this work, after preparing Ti6Al4V/Calcium phosphate (Ti64@CaP) core-shell nanocomposite via a solution-based process, by taking advantage of fused deposition modeling (FDM), porous poly(lactic acid) (PLA)-Ti64@CaP nanocomposite scaffolds were fabricated. Scanning electron microscope (SEM) showed that nanostructured calcium phosphate was distributed uniformly on the surface of Ti64 particles. Also, X-ray diffraction (XRD) indicated that calcium phosphate forms an octacalcium phosphate (OCP) phase. As a result of incorporating 6 wt% Ti64@CaP into the PLA, the compressive modulus and ultimate compressive strength values increased from 1.4 GPa and 29.5 MPa to 2.0 GPa and 53.5 MPa, respectively. Furthermore, the differential scanning calorimetry results revealed an increase in the glass transition temperature of PLA, rising from 57.0 to 62.4 °C, due to the addition of 6 wt% Ti64@CaP. However, it is worth noting that there was a moderate decrease in the crystallization and melting temperatures of the nanocomposite filament, which dropped from 97.

Evidence level

Evidence from laboratory and animal studies provides groundwork for understanding mechanisms and potential before human studies continue.

Browse all related research

Filter the research library by this study's title keywords, author, or publication year.