Mechanical and Biocompatibility Properties of Sintered Titanium Powder for Mimetic 3D-Printed Bone Scaffolds.

Evidence from laboratory and animal studies provides groundwork for understanding mechanisms and potential before human studies continue.

• Level A · Stronger Clinical Evidence
• Level B · Emerging clinical evidence with positive signals
• Level C · Early human research exploring benefits
• Level D · Scientific groundwork from lab and animal studies
• Emerging · Emerging topic under active research

Abstract (original English)

A composite comprising Ti and NaCl powders was sintered similar to a three-dimensional (3D)-printed patient-customized artificial bone scaffold. Additionally, a proper microstructure of the mimetic scaffold and the optimum processing parameters for its development were analyzed. The mechanical properties of the metal-based porous-structured framework used as an artificial bone scaffold were an optimum replacement for the human bone. Thus, it was confirmed that patient-customized scaffolds could be manufactured via 3D printing. The 3D-printed mimetic specimens were fabricated by a powder-sintering method using Ti for the metal parts, NaCl as the pore former, and polylactic acid as the biodegradable binder. Scanning electron microscopy (SEM) images showed that pores were formed homogeneously, while X-ray computed tomography confirmed that open pores were generated. The porosity and pore size distribution were measured using a mercury porosimeter, while the flexural strength and flexural elastic modulus were calculated using the three-point bending test. Based on these measurements, a pore-former content of 15 vol % optimized the density and flexural strength to 2.52 g cm -2 and 283 MPa, respectively, similar to those of the actual iliac bone. According to the 3D-printing production method, a selective laser-sintering process was applied for the fabrication of the mimetic specimen

Evidence level

Evidence from laboratory and animal studies provides groundwork for understanding mechanisms and potential before human studies continue.

Browse all related research

Filter the research library by this study's title keywords, author, or publication year.